wear resistant coatings > BD764 high temperature anti wear erosion resistant coating

BD764 high temperature anti wear erosion resistant coating

BD764 high temperature anti abrasion corrosion resistant ceramic epoxy coating

Product description:

BD764 high temperature anti wear corrosion resistant coating is the high performance interpenetrating network structure
high temperature resistant,abrasion resistant polymeric ceramic material which compounded by high performance wear
resistant,corrosion resistant material(such as: ceramic,silicon carbide,carborundum,titanium alloy etc) and inorganic high
temperature adhesive.Widely used in the preparation of abrasion resistant coating on the surface of various machine parts
which have high temperature,wear resistant requirements.

Product features:
1.With excellent wear resistant and corrosion resistant performance
2.Suitable for the protection of high temperature corrosion and abrasion working condition.
3.The cured products are water resistant,acid and alkali resistant,the cured products don’t shrink,don’t appear crack

Performance Index:

Product item	Physical states	Operation time limit(25℃)	Range of application	Usable time
BD764 high temperature anti wear corrosion resistant coating	paste	5 hours	Used in the preparation of anti abrasion corrosion resistant coating on the surface of various machine part which has high temperature wear resistant requirements under the temperature of 600 degree,such as various dry wet gas flue and holder	Heat for curing, the curing speed is very slow at room temperature
Color	Density (g/cm3)	Compressive strength (Mpa) GB1041-2008	Shear strength (Mpa) GB7124-2008	Working temperature（℃）
Grey	1.8	58	3.6	-60-600

How to use:
1.Surface treatment: Do the roughing treatment on the pending-repair part,grinding with angle grinder or sand blasting etc.The surface after roughing treatment should be cleaned,
the surface after this treatment should be the one roughen,dry and fresh substrates,should be no greasy dirt and dust.

2.Preparation: Mix them according to the weight ratio A:B=2:1,then stir it uniformly,and use it up within 5 hours.

3.Coating: The suitable coating thickness of BD764 high temperature anti wear corrosion resistant coating is 3-5mm,
should make the mixed-up materials be coating on the pending-repair parts.

4.Curing: hot wind curing for 6 hours at the temperature of 80 degree.

Packaging Details:
Packed in a plastic drum, two-component,10Kg/group,A component: 6.7Kg/drum, B component: 3.3Kg/kettle.

Storage and Warranty:
Store it in the cool and dry place,keep away from moisture.The warranty period is 12 months.